Green Silicon Carbide JIS3000 for Fiber Ferrule Lapping
Green Silicon Carbide JIS3000 is a high-purity ultra-fine lapping micropowder professionally engineered for precision fiber ferrule lapping and optical component finishing. Manufactured under strict JIS industrial grading standards, this green SiC powder features ultra-narrow particle size distribution, high purity above 99%, excellent self-sharpening performance and uniform cutting force, making it a core consumable for high-precision optical fiber end-face processing.
Different from ordinary abrasive powders, JIS3000 fine grain size balances efficient material removal and ultra-smooth surface finishing perfectly. It avoids oversized particle scratches, edge chipping and uneven grinding marks that commonly occur in ferrule lapping. With superior hardness and stable mechanical properties, it delivers consistent and delicate lapping effects on ceramic ferrules, zirconia sleeves and optical fiber end faces, ensuring precise geometric dimensions and excellent flatness of fiber connectors.
This green silicon carbide powder boasts outstanding chemical stability, high temperature resistance and low impurity content. It will not cause chemical corrosion, particle embedding or surface contamination during wet lapping and slurry grinding processes. Its excellent dispersion performance enables uniform mixing with lapping liquid, effectively improving lapping efficiency and batch stability, which greatly reduces defective rates in mass optical component production.
Widely applicable for fine lapping and final finishing of SC, LC, FC fiber ferrules and various precision optical ceramic parts, JIS3000 green silicon carbide powder supports high-precision requirements of optical communication component manufacturing. It is a reliable, cost-effective and standard-compliant lapping material for optical factories, helping produce low-loss, high-stability fiber connection products and improve overall product qualification rate.
PHYSICAL PROPERTIES-Green Silicon Carbide JIS3000 for Fiber Ferrule Lapping
| Specific Weight | 3.95 g/ cm3 |
| Mohs Hardness | 9.5 |
| Maximum service temperature | 1900℃ |
| Melting Point | 2250℃ |
TYPICAL CHEMICAL ANALISIS [%]-Green Silicon Carbide JIS3000 for Fiber Ferrule Lapping
| SiC | Fe2O3 | F.C | F.Si | SiO2 | LOI |
| 98.0-99.5 | ≤0.15 | ≤0.30 | ≤0.40 | ≤0.70 | < 0.09 |
PARTICLE SIZE DISTRIBUTION
CHAPTER Ⅰ（JIS STANDARD）
| Size | DO(um) | D3(um) | D50(um) | D94(um) |
| #240 | ≤127 | ≤103 | 57.0±3.0 | ≥40 |
| #280 | ≤112 | ≤87 | 48.0±3.0 | ≥33 |
| #320 | ≤98 | ≤74 | 40.0±2.5 | ≥27 |
| #360 | ≤86 | ≤66 | 35.0±2.0 | ≥23 |
| #400 | ≤75 | ≤58 | 30.0±2.0 | ≥20 |
| #500 | ≤63 | ≤50 | 25.0±2.0 | ≥16 |
| #600 | ≤53 | ≤41 | 20.0±1.5 | ≥13 |
| #700 | ≤45 | ≤37 | 17.0±1.5 | ≥11 |
| #800 | ≤38 | ≤31 | 14.0±1.0 | ≥9.0 |
| #1000 | ≤32 | ≤27 | 11.5±1.0 | ≥7.0 |
| #1200 | ≤27 | ≤23 | 9.5±0.8 | ≥5.5 |
| #1500 | ≤23 | ≤20 | 8.0±0.6 | ≥4.5 |
| #2000 | ≤19 | ≤17 | 6.7±0.6 | ≥4.0 |
| #2500 | ≤16 | ≤14 | 5.5±0.5 | ≥3.0 |
| #3000 | ≤13 | ≤11 | 4.0±0.5 | ≥2.0 |
| #4000 | ≤11 | ≤8.0 | 3.0±0.4 | ≥1.8 |
| #6000 | ≤8.0 | ≤5.0 | 2.0±0.4 | ≥0.8 |
| #8000 | ≤6.0 | ≤3.5 | 1.2±0.3 | ≥0.6 |
CHAPTER Ⅱ（FEPA STANDARD）
| Size | D3(um) | D50(um) | D94（um) |
| F230 | ＜82 | 53.0±3.0 | >34 |
| F240 | ＜70 | 44.5±2.0 | >28 |
| F280 | ＜59 | 36.5±1.5 | >22 |
| F320 | ＜49 | 29.2±1.5 | >16.5 |
| F360 | ＜40 | 22.8±1.5 | >12 |
| F400 | ＜32 | 17.3±1.0 | >8 |
| F500 | ＜25 | 12.8±1.0 | >5 |
| F600 | ＜19 | 9.3±1.0 | >3 |
| F800 | ＜14 | 6.5±1.0 | >2 |
| F1000 | ＜10 | 4.5±0.8 | >1 |
| F1200 | ＜7 | 3.0±0.5 | >1(at 80%) |
| F1500 | ＜5 | 2.0±0.4 | >0.8(at 80%) |
| F2000 | ＜3.5 | 1.2±0.3 | >0.5(at 80%) |
Applications of Green Silicon Carbide JIS3000 in Lapping Industry :
Lapping powder
Lapping slurry
Lapping compound /lapping paste
Optical lapping